Polyurethan zur Herstellung von Slipper und Sandalen
Holen Sie sich aktuelle PreisIncoterm: | FOB,CFR,CIF |
Minimum der Bestellmenge: | 1000 Kilogram |
Transport: | Ocean |
Hafen: | Shanghai |
Incoterm: | FOB,CFR,CIF |
Minimum der Bestellmenge: | 1000 Kilogram |
Transport: | Ocean |
Hafen: | Shanghai |
Modell: A-2260/B-8580
Marke: Xuchuan Chemical
Herkunftsort: China
Arten Von: Kunstharz und Kunststoffe
Application: Outsole and mid-sole
Characteristic: Good handle, low density and good dimension stability
Appearance: Liquid
PRODUKTBESCHREIBUNG
Polyurethan -Rohstoffe
Schuhsohle PU -Chemikalie
Application | shoe sole |
Cream Time (s) | 6~8 |
End of Rise Time (s) | 40~50 |
Free Rise Foam Density(g/cm3) | 0.15~0.25 |
Mold Temperature(℃) | 45~55 |
Demold Time(min) | 2.5~3.5 |
Molded Density (g/cm3) | 0.30~0.45 |
Hardness(Shore A ) | 43~58 |
Tensile strength(MPa) | 1.5~4.5 |
Elongation(%) | 250~400 |
Polyurethan für Schuhe Sohle:
Dichte: 300 ~ 500 kg/m3.
Härte: 45 ~ 75 Shore A.
Gute Kompatibilität mit Pigmenten.
Weit verbreitetes Verhältnis.
Characteristic: Good handle, low density and good dimension stability |
|||||||
Application: Outsole and mid-sole |
|||||||
Typical properties of PU matrix |
|||||||
Name of products |
Appearance |
Viscosity (mPa·s/40℃) |
Density (g·cm-3/40℃) |
Package(kg) |
/ |
/ |
/ |
A-2260 |
Cream white liquid |
800~1200 |
1.01~1.02 |
18 |
/ |
/ |
/ |
B-8580 |
Yellowish transparent liquid or waxy |
600~800 |
1.08~1.2 |
20 |
/ |
/ |
/ |
Materials preheat |
|||||||
A-2260: preheated at 50~60℃ for 8~10 hours |
|||||||
B-8580: preheated at 50~60℃ for 8~12 hours |
|||||||
Typical processing parameters & Reaction parameter |
|||||||
Items |
A/B Materials Temperatures(℃) |
A+C/B Mix ratio (By weight) |
Cream Time (s) |
End of Rise Time (s) |
Free Rise Foam Density(g/cm3) |
Mold Temperature(℃) |
Demold Time(min) |
Parameter |
40~45/38~42 |
100/96~98 |
6~8 |
40~50 |
0.15~0.25 |
45~55 |
2.5~3.5 |
The adding content of C-2 should be 270g±20g/18kg |
|||||||
The adding content of water should be 0~100g/18kg according to the reality |
|||||||
The adding content of hardener should be changed according to the reality |
|||||||
Physical properties |
|||||||
Items |
Molded Density (g/cm3) |
Hardness (Shore A ) |
Tensile strength (MPa) |
Elongation (%) |
Tear Strength (kN/m) |
Ross Flexing (room temperature) ( 40,000 times) |
/ |
/ |
|||||||
/ |
|||||||
Physical properties |
0.30~0.45 |
43~58 |
1.5~4.5 |
250~400 |
10~26 |
No crack |
/ |
Demold time may be prolonged with the increase of sole thickness |
|||||||
These physical data are acquired by testing a sample of 6mm thick. |
|||||||
Data listed above are just for reference. The detail data are subjected to practical production. If other requests for physical properties, please contact us. |
Xuchuan Chemical, das 2007 gegründet wurde, beträgt das Unternehmen ein registriertes Kapital von 500 Millionen RMB. Die Hauptprodukte sind alle Ranges Polyester Polyol, Polyurethanharz für Schuhe, Wasserbasis und lösungsmittelfreie Polyurethanharze für künstliches Leder, Polyurethan-Bindungsklebstoffe und Heißschmelzklebstoffe mit Polyurethan.
Jetzt verfügt Xuchuan über 4 moderne Produktionsbasis, die Produktionskapazität erreichte 630.000 Tonnen pro Jahr, Produkte wurden in 32 Länder und Regionen der Welt exportiert.
Privacy statement: Your privacy is very important to Us. Our company promises not to disclose your personal information to any external company with out your explicit permission.
Fill in more information so that we can get in touch with you faster
Privacy statement: Your privacy is very important to Us. Our company promises not to disclose your personal information to any external company with out your explicit permission.